EN AW-1050A 0.6 x 1000 x 2000 mm
EN AW-1050A
It is the most pure form of aluminium and the most common plate alloy. The alloy has a good property regarding bending and welding, and it is suitable for surface treatment.
It contains 99.5 % aluminium, and they mainly produce it in thickness from 0.5 mm - 6 mm.
EN AW-1050A DDQ:
It contains 99,5% aluminum and is produced in a very soft temper, making it suitable for deep drawing applications. Mainly produced in thickness 1,00 mm, 1,25 m, 1,05 mm and 2,00 mm.
We are not liable for items out of stock. The specified weight is theoretical. Please contact us if you have any further enquiries.
Alloys
Density | Si | Fe | Cu | Mn | Mg | Zn | Ti | Other | |||
---|---|---|---|---|---|---|---|---|---|---|---|
Name | g/cm3 | Max | Max | Max | Max | Min | Max | Max | Max | Max | Rest |
EN AW-1050A | 2.7 | 0.25 | 0.4 | 0.05 | 0.05 | 0.05 | 0.05 | 0.07 | 0.05 | 0.03 | Al, Aluminium |
Aluminium Properties
Thermal conductivity | Coefficient of thermal expansion | Melting point | Elastic modulus | Electrical conductivity | |||
---|---|---|---|---|---|---|---|
Alloy | Temper | W/m*K | µm/(m*K) | min °C | KN/mm2 | %IACS | |
EN AW-1050A | Hx2 | 229 | 23.5 | 645 | 658 | 69 | 59.5 |
EN AW-1050A | Hx4 | 229 | 23.5 | 645 | 658 | 69 | 59.5 |
EN AW-1050A | Hx6 | 229 | 23.5 | 645 | 658 | 69 | 59.5 |
EN AW-1050A | Hx8 | 229 | 23.5 | 645 | 658 | 69 | 59.5 |
EN AW-1050A | Hx9 | 229 | 23.5 | 645 | 658 | 69 | 59.5 |
EN AW-1050A | O | 229 | 23.5 | 645 | 658 | 69 | 59.5 |
Mechanical properties
Tensile strength (Rm) MPa | Proof stress (Rp0,2) | Elongation | Brinell Hardness | Thickness interval | Elongation A50mm | Bend radius 90° | Bend radius 180° | |||||
---|---|---|---|---|---|---|---|---|---|---|---|---|
Norm | Alloy | Temper | Rm N/mm2 | MPa | % min | HBS | mm | % min | t | t | ||
EN 485-2:2008 | EN AW-1050A | H14 | 105 | 145 | 85 | - | 34 | 0.2 | 0.5 | 2 | 0 | 1 |
EN 485-2:2008 | EN AW-1050A | H14 | 105 | 145 | 85 | - | 34 | 0.5 | 1.5 | 2 | 0.5 | 1 |
EN 485-2:2008 | EN AW-1050A | H14 | 105 | 145 | 85 | - | 34 | 1.5 | 3 | 4 | 1 | 1 |
EN 485-2:2008 | EN AW-1050A | H14 | 105 | 145 | 85 | - | 34 | 3 | 6 | 5 | 1.5 | - |
EN 485-2:2008 | EN AW-1050A | H14 | 105 | 145 | 85 | - | 34 | 6 | 12.5 | 6 | 2.5 | - |
EN 485-2:2008 | EN AW-1050A | H14 | 105 | 145 | 85 | 6 | 34 | 12.5 | 25 | - | - | - |
EN 485-2:2008 | EN AW-1050A | H24 | 105 | 145 | 75 | - | 33 | 0.2 | 0.5 | 3 | 0 | 1 |
EN 485-2:2008 | EN AW-1050A | H24 | 105 | 145 | 75 | - | 33 | 0.5 | 1.5 | 4 | 0.5 | 1 |
EN 485-2:2008 | EN AW-1050A | H24 | 105 | 145 | 75 | - | 33 | 1.5 | 3 | 5 | 1 | 1 |
EN 485-2:2008 | EN AW-1050A | H24 | 105 | 145 | 75 | - | 33 | 3 | 6 | 8 | 1.5 | 1.5 |
EN 485-2:2008 | EN AW-1050A | H24 | 105 | 145 | 75 | - | 33 | 6 | 12.5 | 8 | 2.5 | - |