EN AW-5754

Material id: 1000872

Plate length

1000 x 2000 mm

Thickness excl. pattern

2/4 mm

Temper

H114

We stock profound ranges of tread plates, which we all can deliver with quintet pattern. Therefore, be aware that the thickness of the plates are measured without the pattern height, and therefore a 5/7 tread plate has a plate thickness of 5 mm and a pattern height of 2.0 mm.

Do you request other types than the once introduced - you are welcome to contact us.


  • Plate length: 1000 x 2000 mm
  • Thickness excl. pattern: 2/4 mm
  • Temper: H114
  • Weight: 13 kg
  • Weldability: High
  • Corrosion: High
  • Cut/drilling: High
  • Surface: Medium

EN AW-5754

It is sea water resistant and has an average strength, high corrosion resistance and good for welding Medium for anodizing.


We are not liable for items out of stock. The specified weight is theoretical. Please contact us if you have any further enquiries.

Alloy - Alloys

Si
Min
-
Max
0.4
Fe
Min
-
Max
0.4
Cu
Min
-
Max
0.1
Mn
Min
-
Max
0.5
Mg
Min
2.6
Max
3.6
Cr
Min
-
Max
0.3
Zn
Min
-
Max
0.2
Ti
Min
-
Max
0.15
Others
Min
0.15
Max
-

Alloy - Aluminium Properties

Alloy
EN AW-5754
Temper
Hx2
Thermal conductivity
W/m*K
132
Coefficient of thermal expansion
µm/(m*K)
23,7
Annealing
Min
-
Annealing
Max
-
Melting point
Min
595
Max
645
Melting point
Max
645
Elastic modulus
KN/mm2
70
Electrical conductivity
%IACS
32,5
Alloy
EN AW-5754
Temper
Hx4
Thermal conductivity
W/m*K
132
Coefficient of thermal expansion
µm/(m*K)
23,7
Annealing
Min
-
Annealing
Max
-
Melting point
Min
595
Max
645
Melting point
Max
645
Elastic modulus
KN/mm2
70
Electrical conductivity
%IACS
32,5
Alloy
EN AW-5754
Temper
Hx6
Thermal conductivity
W/m*K
132
Coefficient of thermal expansion
µm/(m*K)
23,7
Annealing
Min
-
Annealing
Max
-
Melting point
Min
595
Max
645
Melting point
Max
645
Elastic modulus
KN/mm2
70
Electrical conductivity
%IACS
32,5
Alloy
EN AW-5754
Temper
Hx8
Thermal conductivity
W/m*K
132
Coefficient of thermal expansion
µm/(m*K)
23,7
Annealing
Min
-
Annealing
Max
-
Melting point
Min
595
Max
645
Melting point
Max
645
Elastic modulus
KN/mm2
70
Electrical conductivity
%IACS
32,5
Alloy
EN AW-5754
Temper
Hx9
Thermal conductivity
W/m*K
-
Coefficient of thermal expansion
µm/(m*K)
23,7
Annealing
Min
-
Annealing
Max
-
Melting point
Min
595
Max
645
Melting point
Max
645
Elastic modulus
KN/mm2
70
Electrical conductivity
%IACS
-
Alloy
EN AW-5754
Temper
O
Thermal conductivity
W/m*K
132
Coefficient of thermal expansion
µm/(m*K)
23,7
Annealing
Min
-
Annealing
Max
-
Melting point
Min
595
Max
645
Melting point
Max
645
Elastic modulus
KN/mm2
70
Electrical conductivity
%IACS
32,5