EN AW-3003

Material id: 1141313

Ral 9005

Plate length

1500 x 3000 mm

Thickness

1.0 mm

Shine

Matte

We stock a wide range of painted plates in standard thickness between 0,6 mm and 2 mm. Our standard range features the most popular paintings, but if you request another thickness or colours - you are welcome to contact us.  


  • Plate length: 1500 x 3000 mm
  • Thickness: 1.0 mm
  • Shine: Matte
  • Weldability: High
  • Corrosion: High
  • Cut/drilling: Low
  • Surface: Medium

EN AW-3003

Eine Manganlegierung mit hoher Korrosionsbeständigkeit. Die Legierung hat eine durchschnittliche Festigkeit und eignet sich zum Schweißen und Biegen.


We are not liable for items out of stock. The specified weight is theoretical. Please contact us if you have any further enquiries.

Alloy - Alloys

Si
Min
-
Max
0.6
Fe
Min
-
Max
0.7
Cu
Min
0.05
Max
0.2
Mn
Min
1
Max
1.5
Zn
Min
-
Max
0.1
Others
Min
0.15
Max
-

Alloy - Aluminium Properties

Alloy
EN AW-3003
Temper
Hx2
Thermal conductivity
W/m*K
160
Coefficient of thermal expansion
µm/(m*K)
23,1
Annealing
Min
-
Annealing
Max
-
Melting point
Min
640
Max
655
Melting point
Max
655
Elastic modulus
KN/mm2
70
Electrical conductivity
%IACS
42
Alloy
EN AW-3003
Temper
Hx4
Thermal conductivity
W/m*K
160
Coefficient of thermal expansion
µm/(m*K)
23,1
Annealing
Min
-
Annealing
Max
-
Melting point
Min
640
Max
655
Melting point
Max
655
Elastic modulus
KN/mm2
70
Electrical conductivity
%IACS
42
Alloy
EN AW-3003
Temper
Hx6
Thermal conductivity
W/m*K
160
Coefficient of thermal expansion
µm/(m*K)
23,1
Annealing
Min
-
Annealing
Max
-
Melting point
Min
640
Max
655
Melting point
Max
655
Elastic modulus
KN/mm2
70
Electrical conductivity
%IACS
42
Alloy
EN AW-3003
Temper
Hx8
Thermal conductivity
W/m*K
160
Coefficient of thermal expansion
µm/(m*K)
23,1
Annealing
Min
-
Annealing
Max
-
Melting point
Min
640
Max
655
Melting point
Max
655
Elastic modulus
KN/mm2
70
Electrical conductivity
%IACS
42
Alloy
EN AW-3003
Temper
Hx9
Thermal conductivity
W/m*K
160
Coefficient of thermal expansion
µm/(m*K)
23,1
Annealing
Min
-
Annealing
Max
-
Melting point
Min
640
Max
655
Melting point
Max
655
Elastic modulus
KN/mm2
70
Electrical conductivity
%IACS
42
Alloy
EN AW-3003
Temper
O
Thermal conductivity
W/m*K
190
Coefficient of thermal expansion
µm/(m*K)
23,1
Annealing
Min
-
Annealing
Max
-
Melting point
Min
640
Max
655
Melting point
Max
655
Elastic modulus
KN/mm2
70
Electrical conductivity
%IACS
50,5