EN AW-5005

Ral 9005

Width

1000.0 mm

Thickness

0.7 mm

Shine

Matte

Weight

250.0 mm

We offer coils in the standard thickness from 0.63 mm to 1 mm. We deliver all our coils in the standard width of 1000 mm and basic, we can deliver in three standard sizes: 250 kg, 500 kg and 1000 kg. If you request further information or other dimensions - you are welcome to contact us.


  • Width: 1000.0 mm
  • Thickness: 0.7 mm
  • Shine: Matte
  • Weight: 250.0 mm
  • Weldability: High
  • Corrosion: High
  • Cut/drilling: Medium
  • Surface: High
On request

EN AW-5005

It is good for machining and bending and has a high corrosion resistance and good for welding. The alloy is very suitable for decorative anodizing.


We are not liable for items out of stock. The specified weight is theoretical. Please contact us if you have any further enquiries.

Alloy - Alloys

Si
Min
-
Max
0.3
Fe
Min
-
Max
0.7
Cu
Min
-
Max
0.2
Mn
Min
-
Max
0.2
Mg
Min
0.5
Max
1.1
Cr
Min
-
Max
0.1
Zn
Min
-
Max
0.25
Others
Min
0.15
Max
-

Alloy - Aluminium Properties

Alloy
EN AW-5005
Temper
Hx2
Thermal conductivity
W/m*K
201
Coefficient of thermal expansion
µm/(m*K)
23,5
Annealing
Min
-
Annealing
Max
-
Melting point
Min
630
Max
655
Melting point
Max
655
Elastic modulus
KN/mm2
70
Electrical conductivity
%IACS
52
Alloy
EN AW-5005
Temper
Hx4
Thermal conductivity
W/m*K
201
Coefficient of thermal expansion
µm/(m*K)
23,5
Annealing
Min
-
Annealing
Max
-
Melting point
Min
630
Max
655
Melting point
Max
655
Elastic modulus
KN/mm2
70
Electrical conductivity
%IACS
52
Alloy
EN AW-5005
Temper
Hx6
Thermal conductivity
W/m*K
201
Coefficient of thermal expansion
µm/(m*K)
23,5
Annealing
Min
-
Annealing
Max
-
Melting point
Min
630
Max
655
Melting point
Max
655
Elastic modulus
KN/mm2
70
Electrical conductivity
%IACS
52
Alloy
EN AW-5005
Temper
Hx8
Thermal conductivity
W/m*K
201
Coefficient of thermal expansion
µm/(m*K)
23,5
Annealing
Min
-
Annealing
Max
-
Melting point
Min
630
Max
655
Melting point
Max
655
Elastic modulus
KN/mm2
70
Electrical conductivity
%IACS
52
Alloy
EN AW-5005
Temper
Hx9
Thermal conductivity
W/m*K
201
Coefficient of thermal expansion
µm/(m*K)
23,5
Annealing
Min
-
Annealing
Max
-
Melting point
Min
630
Max
655
Melting point
Max
655
Elastic modulus
KN/mm2
70
Electrical conductivity
%IACS
52
Alloy
EN AW-5005
Temper
O
Thermal conductivity
W/m*K
201
Coefficient of thermal expansion
µm/(m*K)
23,5
Annealing
Min
-
Annealing
Max
-
Melting point
Min
630
Max
655
Melting point
Max
655
Elastic modulus
KN/mm2
70
Electrical conductivity
%IACS
52