EN AW-1050A

Width

1000.0 mm

Thickness

0.88 mm

Weight

250.0 mm

We offer coils in the standard thickness from 0.63 mm to 1 mm. We deliver all our coils in the standard width of 1000 mm and basic, we can deliver in three standard sizes: 250 kg, 500 kg and 1000 kg. If you request further information or other dimensions - you are welcome to contact us.


  • Width: 1000.0 mm
  • Thickness: 0.88 mm
  • Weight: 250.0 mm
  • Weldability: High
  • Corrosion: High
  • Cut/drilling: Medium
  • Surface: High
On request

EN AW-1050A

It is the most pure form of aluminium and the most common plate alloy. The alloy has a good property regarding bending and welding, and it is suitable for surface treatment.

It contains 99.5 % aluminium, and they mainly produce it in thickness from 0.5 mm - 6 mm.

EN AW-1050A DDQ:

It contains 99,5% aluminum and is produced in a very soft temper, making it suitable for deep drawing applications. Mainly produced in thickness 1,00 mm, 1,25 m, 1,05 mm and 2,00 mm.


We are not liable for items out of stock. The specified weight is theoretical. Please contact us if you have any further enquiries.

Alloy - Alloys

Si
Min
0.25
Max
0.25
Fe
Min
-
Max
0.4
Cu
Min
0.05
Max
0.05
Mn
Min
0.01
Max
0.01
Mg
Min
0.05
Max
0.05
Zn
Min
-
Max
0.07
Ti
Min
-
Max
0.05
Others
Min
0.03
Max
-
Al
Min
99.5
Max
-

Alloy - Aluminium Properties

Alloy
EN AW-1050A
Temper
Hx2
Thermal conductivity
W/m*K
229
Coefficient of thermal expansion
µm/(m*K)
23,5
Annealing
Min
-
Annealing
Max
-
Melting point
Min
645
Max
658
Melting point
Max
658
Elastic modulus
KN/mm2
69
Electrical conductivity
%IACS
59,5
Alloy
EN AW-1050A
Temper
Hx4
Thermal conductivity
W/m*K
229
Coefficient of thermal expansion
µm/(m*K)
23,5
Annealing
Min
-
Annealing
Max
-
Melting point
Min
645
Max
658
Melting point
Max
658
Elastic modulus
KN/mm2
69
Electrical conductivity
%IACS
59,5
Alloy
EN AW-1050A
Temper
Hx6
Thermal conductivity
W/m*K
229
Coefficient of thermal expansion
µm/(m*K)
23,5
Annealing
Min
-
Annealing
Max
-
Melting point
Min
645
Max
658
Melting point
Max
658
Elastic modulus
KN/mm2
69
Electrical conductivity
%IACS
59,5
Alloy
EN AW-1050A
Temper
Hx8
Thermal conductivity
W/m*K
229
Coefficient of thermal expansion
µm/(m*K)
23,5
Annealing
Min
-
Annealing
Max
-
Melting point
Min
645
Max
658
Melting point
Max
658
Elastic modulus
KN/mm2
69
Electrical conductivity
%IACS
59,5
Alloy
EN AW-1050A
Temper
Hx9
Thermal conductivity
W/m*K
229
Coefficient of thermal expansion
µm/(m*K)
23,5
Annealing
Min
-
Annealing
Max
-
Melting point
Min
645
Max
658
Melting point
Max
658
Elastic modulus
KN/mm2
69
Electrical conductivity
%IACS
59,5
Alloy
EN AW-1050A
Temper
O
Thermal conductivity
W/m*K
229
Coefficient of thermal expansion
µm/(m*K)
23,5
Annealing
Min
-
Annealing
Max
-
Melting point
Min
645
Max
658
Melting point
Max
658
Elastic modulus
KN/mm2
69
Electrical conductivity
%IACS
59,5