EN AW-6082

Material id: 1079285

Diameter

10 mm

Length

3000.0 mm

Process

Drawn

We stock a wide range of round bars in 2000 og 6000 alloys Essentially, they exist in all sizes from 5 mm and up to 500 mm in diameter, and often in lengths of 3000 mm and 6000 mm and in three different qualities: pressed, drawn and moulded. If you request other dimensions than the once introduced - you are welcome to contact us


  • Diameter: 10 mm
  • Length: 3000.0 mm
  • Process:
  • Weight: 0.21kg
  • Weldability: Medium
  • Corrosion: High
  • Cut/drilling: Medium
  • Surface: Medium
In stock

EN AW-6082

Has a high strength and a good corrosion resistance. The alloy is good for welding, and you can anodize it. 


We are not liable for items out of stock. The specified weight is theoretical. Please contact us if you have any further enquiries.

Alloy - Alloys

Si
Min
0.7
Max
1.3
Fe
Min
-
Max
0.5
Cu
Min
-
Max
0.1
Mn
Min
0.4
Max
1
Mg
Min
0.6
Max
1.2
Cr
Min
-
Max
0.25
Zn
Min
-
Max
0.2
Ti
Min
-
Max
0.1
Others
Min
0.15
Max
-

Alloy - Aluminium Properties

Alloy
EN AW-6082
Temper
O
Thermal conductivity
W/m*K
216,0
Coefficient of thermal expansion
µm/(m*K)
23,1
Annealing
Min
-
Annealing
Max
-
Melting point
Min
575
Max
650
Melting point
Max
650
Elastic modulus
KN/mm2
70000
Electrical conductivity
%IACS
55,5
Alloy
EN AW-6082
Temper
T1
Thermal conductivity
W/m*K
-
Coefficient of thermal expansion
µm/(m*K)
23,1
Annealing
Min
-
Annealing
Max
-
Melting point
Min
575
Max
650
Melting point
Max
650
Elastic modulus
KN/mm2
70000
Electrical conductivity
%IACS
-
Alloy
EN AW-6082
Temper
T4
Thermal conductivity
W/m*K
167,0
Coefficient of thermal expansion
µm/(m*K)
23,1
Annealing
Min
-
Annealing
Max
-
Melting point
Min
575
Max
650
Melting point
Max
650
Elastic modulus
KN/mm2
70000
Electrical conductivity
%IACS
42,0
Alloy
EN AW-6082
Temper
T5
Thermal conductivity
W/m*K
-
Coefficient of thermal expansion
µm/(m*K)
23,1
Annealing
Min
-
Annealing
Max
-
Melting point
Min
575
Max
650
Melting point
Max
650
Elastic modulus
KN/mm2
70000
Electrical conductivity
%IACS
-
Alloy
EN AW-6082
Temper
T6
Thermal conductivity
W/m*K
172,0
Coefficient of thermal expansion
µm/(m*K)
23,1
Annealing
Min
-
Annealing
Max
-
Melting point
Min
575
Max
650
Melting point
Max
650
Elastic modulus
KN/mm2
70000
Electrical conductivity
%IACS
44,0

Alloy - Mechanical Properties (EN 754-2:2013)

Dimension
Min
0
Max
80
Tensile strength (Rm) MPa
Min
205
Max
-
Proof stress (Rp0,2)
MPa
110
Elongation A50
% min
14
Elongation A
% min
12
Brinell hardness
HBS
70
Dimension
Min
0
Max
80
Tensile strength (Rm) MPa
Min
310
Max
-
Proof stress (Rp0,2)
MPa
255
Elongation A50
% min
10
Elongation A
% min
9
Brinell hardness
HBS
95