EN AW-5754

175 mm

Diameter

175.0 mm

Length

3000.0 mm

Process

Extruded

We stock a wide range of round bars in 2000 og 6000 alloys Essentially, they exist in all sizes from 5 mm and up to 500 mm in diameter, and often in lengths of 3000 mm and 6000 mm and in three different qualities: pressed, drawn and moulded. If you request other dimensions than the once introduced - you are welcome to contact us


  • Diameter: 175.0 mm
  • Length: 3000.0 mm
  • Process: Extruded
  • Weight: 64 kg
  • Weldability: High
  • Corrosion: High
  • Cut/drilling: High
  • Surface: Medium
On request

EN AW-5754

It is sea water resistant and has an average strength, high corrosion resistance and good for welding Medium for anodizing.


We are not liable for items out of stock. The specified weight is theoretical. Please contact us if you have any further enquiries.

Alloy - Alloys

Si
Min
-
Max
0.4
Fe
Min
-
Max
0.4
Cu
Min
-
Max
0.1
Mn
Min
-
Max
0.5
Mg
Min
2.6
Max
3.6
Cr
Min
-
Max
0.3
Zn
Min
-
Max
0.2
Ti
Min
-
Max
0.15
Others
Min
0.15
Max
-

Alloy - Aluminium Properties

Alloy
EN AW-5754
Temper
Hx2
Thermal conductivity
W/m*K
132
Coefficient of thermal expansion
µm/(m*K)
23,7
Annealing
Min
-
Annealing
Max
-
Melting point
Min
595
Max
645
Melting point
Max
645
Elastic modulus
KN/mm2
70
Electrical conductivity
%IACS
32,5
Alloy
EN AW-5754
Temper
Hx4
Thermal conductivity
W/m*K
132
Coefficient of thermal expansion
µm/(m*K)
23,7
Annealing
Min
-
Annealing
Max
-
Melting point
Min
595
Max
645
Melting point
Max
645
Elastic modulus
KN/mm2
70
Electrical conductivity
%IACS
32,5
Alloy
EN AW-5754
Temper
Hx6
Thermal conductivity
W/m*K
132
Coefficient of thermal expansion
µm/(m*K)
23,7
Annealing
Min
-
Annealing
Max
-
Melting point
Min
595
Max
645
Melting point
Max
645
Elastic modulus
KN/mm2
70
Electrical conductivity
%IACS
32,5
Alloy
EN AW-5754
Temper
Hx8
Thermal conductivity
W/m*K
132
Coefficient of thermal expansion
µm/(m*K)
23,7
Annealing
Min
-
Annealing
Max
-
Melting point
Min
595
Max
645
Melting point
Max
645
Elastic modulus
KN/mm2
70
Electrical conductivity
%IACS
32,5
Alloy
EN AW-5754
Temper
Hx9
Thermal conductivity
W/m*K
-
Coefficient of thermal expansion
µm/(m*K)
23,7
Annealing
Min
-
Annealing
Max
-
Melting point
Min
595
Max
645
Melting point
Max
645
Elastic modulus
KN/mm2
70
Electrical conductivity
%IACS
-
Alloy
EN AW-5754
Temper
O
Thermal conductivity
W/m*K
132
Coefficient of thermal expansion
µm/(m*K)
23,7
Annealing
Min
-
Annealing
Max
-
Melting point
Min
595
Max
645
Melting point
Max
645
Elastic modulus
KN/mm2
70
Electrical conductivity
%IACS
32,5

Alloy - Mechanical Properties (EN 755-2:2013)

Dimension
Min
0
Max
150
Tensile strength (Rm) MPa
Min
180
Max
250
Proof stress (Rp0,2)
MPa
80
Elongation A50
% min
17
Elongation A
% min
15
Brinell hardness
HBS
45
Dimension
Min
0
Max
150
Tensile strength (Rm) MPa
Min
180
Max
-
Proof stress (Rp0,2)
MPa
80
Elongation A50
% min
14
Elongation A
% min
12
Brinell hardness
HBS
47
Dimension
Min
150
Max
250
Tensile strength (Rm) MPa
Min
180
Max
-
Proof stress (Rp0,2)
MPa
70
Elongation A50
% min
13
Elongation A
% min
-
Brinell hardness
HBS
47
Dimension
Min
0
Max
150
Tensile strength (Rm) MPa
Min
180
Max
250
Proof stress (Rp0,2)
MPa
80
Elongation A50
% min
17
Elongation A
% min
15
Brinell hardness
HBS
45