EN AW-5083

120 mm

Diameter

120.0 mm

Length

3000.0 mm

Process

Extruded

We stock a wide range of round bars in 2000 og 6000 alloys Essentially, they exist in all sizes from 5 mm and up to 500 mm in diameter, and often in lengths of 3000 mm and 6000 mm and in three different qualities: pressed, drawn and moulded. If you request other dimensions than the once introduced - you are welcome to contact us


  • Diameter: 120.0 mm
  • Length: 3000.0 mm
  • Process: Extruded
  • Weight: 30 kg
  • Weldability: High
  • Corrosion: High
  • Cut/drilling: High
  • Surface: Medium
On request

EN AW-5083

It is sea water resistant and has an average strength, high corrosion resistance and good for welding Medium for anodizing

 


We are not liable for items out of stock. The specified weight is theoretical. Please contact us if you have any further enquiries.

Alloy - Alloys

Si
Min
-
Max
0.4
Fe
Min
-
Max
0.4
Cu
Min
-
Max
0.1
Mn
Min
0.4
Max
1
Mg
Min
4
Max
4.9
Cr
Min
0.05
Max
0.25
Zn
Min
-
Max
0.25
Ti
Min
-
Max
0.15
Others
Min
0.15
Max
-

Alloy - Aluminium Properties

Alloy
EN AW-5083
Temper
Hx2
Thermal conductivity
W/m*K
117
Coefficient of thermal expansion
µm/(m*K)
23,8
Annealing
Min
-
Annealing
Max
-
Melting point
Min
580
Max
640
Melting point
Max
640
Elastic modulus
KN/mm2
71
Electrical conductivity
%IACS
28,5
Alloy
EN AW-5083
Temper
Hx4
Thermal conductivity
W/m*K
117
Coefficient of thermal expansion
µm/(m*K)
23,8
Annealing
Min
-
Annealing
Max
-
Melting point
Min
580
Max
640
Melting point
Max
640
Elastic modulus
KN/mm2
71
Electrical conductivity
%IACS
28,5
Alloy
EN AW-5083
Temper
Hx6
Thermal conductivity
W/m*K
117
Coefficient of thermal expansion
µm/(m*K)
23,8
Annealing
Min
-
Annealing
Max
-
Melting point
Min
580
Max
640
Melting point
Max
640
Elastic modulus
KN/mm2
71
Electrical conductivity
%IACS
28,5
Alloy
EN AW-5083
Temper
Hx8
Thermal conductivity
W/m*K
117
Coefficient of thermal expansion
µm/(m*K)
23,8
Annealing
Min
-
Annealing
Max
-
Melting point
Min
580
Max
640
Melting point
Max
640
Elastic modulus
KN/mm2
71
Electrical conductivity
%IACS
28,5
Alloy
EN AW-5083
Temper
Hx9
Thermal conductivity
W/m*K
-
Coefficient of thermal expansion
µm/(m*K)
23,8
Annealing
Min
-
Annealing
Max
-
Melting point
Min
580
Max
640
Melting point
Max
640
Elastic modulus
KN/mm2
71
Electrical conductivity
%IACS
-
Alloy
EN AW-5083
Temper
O
Thermal conductivity
W/m*K
117
Coefficient of thermal expansion
µm/(m*K)
23,8
Annealing
Min
-
Annealing
Max
-
Melting point
Min
580
Max
640
Melting point
Max
640
Elastic modulus
KN/mm2
71
Electrical conductivity
%IACS
28,5

Alloy - Mechanical Properties (EN 755-2:2013)

Dimension
Min
0
Max
200
Tensile strength (Rm) MPa
Min
270
Max
-
Proof stress (Rp0,2)
MPa
110
Elongation A50
% min
12
Elongation A
% min
10
Brinell hardness
HBS
70
Dimension
Min
0
Max
200
Tensile strength (Rm) MPa
Min
270
Max
-
Proof stress (Rp0,2)
MPa
125
Elongation A50
% min
12
Elongation A
% min
10
Brinell hardness
HBS
70
Dimension
Min
0
Max
200
Tensile strength (Rm) MPa
Min
270
Max
-
Proof stress (Rp0,2)
MPa
110
Elongation A50
% min
12
Elongation A
% min
10
Brinell hardness
HBS
70