EN AW-2011

145 mm

Diameter

145.0 mm

Length

3000.0 mm

Process

Extruded

We stock a wide range of round bars in 2000 og 6000 alloys Essentially, they exist in all sizes from 5 mm and up to 500 mm in diameter, and often in lengths of 3000 mm and 6000 mm and in three different qualities: pressed, drawn and moulded. If you request other dimensions than the once introduced - you are welcome to contact us


  • Diameter: 145.0 mm
  • Length: 3000.0 mm
  • Process: Extruded
  • Weight: 46 kg
  • Weldability: Low
  • Corrosion: Low
  • Cut/drilling: High
  • Surface: Low
On request

EN AW-2011

A copper alloy that typically contains between 4.0 and 5.0 % copper, and it is suitable for producing machine parts, bolts and rivets. It looks very much like an EN AW-2007, but it is a bit softer. It is a short-chipped alloy, which is suitable for treatment, threads and high machining speeds and gives a shiny surface after treatment. It has a high strength against metal fatigue. The alloy has an inferior corrosion resistance, and it is not suitable for welding because of the high content of copper. It is possibly approved after the ROHS.


We are not liable for items out of stock. The specified weight is theoretical. Please contact us if you have any further enquiries.

Alloy - Alloys

Si
Min
-
Max
0.4
Fe
Min
-
Max
0.8
Cu
Min
3.3
Max
4.6
Mn
Min
0.5
Max
1
Mg
Min
0.4
Max
1.8
Cr
Min
-
Max
0.1
Zn
Min
-
Max
0.2
Bi
Min
0.2
Max
0.6
Pb
Min
0.2
Max
0.6
Others
Min
0.3
Max
-

Alloy - Aluminium Properties

Alloy
EN AW-2011
Temper
T3
Thermal conductivity
W/m*K
152
Coefficient of thermal expansion
µm/(m*K)
23
Annealing
Min
-
Annealing
Max
-
Melting point
Min
540
Max
645
Melting point
Max
645
Elastic modulus
KN/mm2
72
Electrical conductivity
%IACS
39
Alloy
EN AW-2011
Temper
T4
Thermal conductivity
W/m*K
152
Coefficient of thermal expansion
µm/(m*K)
23
Annealing
Min
-
Annealing
Max
-
Melting point
Min
540
Max
645
Melting point
Max
645
Elastic modulus
KN/mm2
72
Electrical conductivity
%IACS
39
Alloy
EN AW-2011
Temper
T6
Thermal conductivity
W/m*K
172
Coefficient of thermal expansion
µm/(m*K)
23
Annealing
Min
-
Annealing
Max
-
Melting point
Min
540
Max
645
Melting point
Max
645
Elastic modulus
KN/mm2
72
Electrical conductivity
%IACS
45,5
Alloy
EN AW-2011
Temper
T8
Thermal conductivity
W/m*K
172
Coefficient of thermal expansion
µm/(m*K)
23
Annealing
Min
-
Annealing
Max
-
Melting point
Min
540
Max
645
Melting point
Max
645
Elastic modulus
KN/mm2
72
Electrical conductivity
%IACS
45,5

Alloy - Mechanical Properties (EN 755-2:2013)

Dimension
Min
-
Max
60
Tensile strength (Rm) MPa
Min
275
Max
-
Proof stress (Rp0,2)
MPa
125
Elongation A50
% min
12
Elongation A
% min
14
Brinell hardness
HBS
95
Dimension
Min
-
Max
200
Tensile strength (Rm) MPa
Min
275
Max
-
Proof stress (Rp0,2)
MPa
125
Elongation A50
% min
12
Elongation A
% min
14
Brinell hardness
HBS
95
Dimension
Min
-
Max
75
Tensile strength (Rm) MPa
Min
310
Max
-
Proof stress (Rp0,2)
MPa
230
Elongation A50
% min
6
Elongation A
% min
8
Brinell hardness
HBS
110
Dimension
Min
-
Max
60
Tensile strength (Rm) MPa
Min
310
Max
-
Proof stress (Rp0,2)
MPa
230
Elongation A50
% min
6
Elongation A
% min
8
Brinell hardness
HBS
110
Dimension
Min
75
Max
200
Tensile strength (Rm) MPa
Min
295
Max
-
Proof stress (Rp0,2)
MPa
195
Elongation A50
% min
-
Elongation A
% min
6
Brinell hardness
HBS
110