EN AW-6082

Material id: 1027313

Width

35.0 mm

Length

3000.0 mm

Process

Extruded

We have a profound stock range of square bars, and mainly we offer them in 2000 and 6000 alloys. Essentially, they exist in all sizes from 8 mm and up to 200 mm and often in lengths of 3000 mm and 6000 mm. If you request other dimensions or alloy types than the once introduced - you are welcome to contact us.


  • Width: 35.0 mm
  • Length: 3000.0 mm
  • Process: Extruded
  • Weldability: Medium
  • Corrosion: High
  • Cut/drilling: Medium
  • Surface: Medium

EN AW-6082

Has a high strength and a good corrosion resistance. The alloy is good for welding, and you can anodize it. 


We are not liable for items out of stock. The specified weight is theoretical. Please contact us if you have any further enquiries.

Alloy - Alloys

Si
Min
0.7
Max
1.3
Fe
Min
-
Max
0.5
Cu
Min
-
Max
0.1
Mn
Min
0.4
Max
1
Mg
Min
0.6
Max
1.2
Cr
Min
-
Max
0.25
Zn
Min
-
Max
0.2
Ti
Min
-
Max
0.1
Others
Min
0.15
Max
-

Alloy - Aluminium Properties

Alloy
EN AW-6082
Temper
O
Thermal conductivity
W/m*K
216
Coefficient of thermal expansion
µm/(m*K)
23,1
Annealing
Min
-
Annealing
Max
-
Melting point
Min
575
Max
650
Melting point
Max
650
Elastic modulus
KN/mm2
70
Electrical conductivity
%IACS
55,5
Alloy
EN AW-6082
Temper
T1
Thermal conductivity
W/m*K
-
Coefficient of thermal expansion
µm/(m*K)
23,1
Annealing
Min
-
Annealing
Max
-
Melting point
Min
575
Max
650
Melting point
Max
650
Elastic modulus
KN/mm2
70
Electrical conductivity
%IACS
-
Alloy
EN AW-6082
Temper
T4
Thermal conductivity
W/m*K
167
Coefficient of thermal expansion
µm/(m*K)
23,1
Annealing
Min
-
Annealing
Max
-
Melting point
Min
575
Max
650
Melting point
Max
650
Elastic modulus
KN/mm2
70
Electrical conductivity
%IACS
42
Alloy
EN AW-6082
Temper
T5
Thermal conductivity
W/m*K
-
Coefficient of thermal expansion
µm/(m*K)
23,1
Annealing
Min
-
Annealing
Max
-
Melting point
Min
575
Max
650
Melting point
Max
650
Elastic modulus
KN/mm2
70
Electrical conductivity
%IACS
-
Alloy
EN AW-6082
Temper
T6
Thermal conductivity
W/m*K
172
Coefficient of thermal expansion
µm/(m*K)
23,1
Annealing
Min
-
Annealing
Max
-
Melting point
Min
575
Max
650
Melting point
Max
650
Elastic modulus
KN/mm2
70
Electrical conductivity
%IACS
44

Alloy - Mechanical Properties (EN 485-2:2008)

Thickness interval
Min
0.4
Max
1.5
Tensile strength (Rm) MPa
Min
310
Max
-
Proof stress (Rp0,2)
MPa
260
Elongation A50mm
% min
6
Elongation
% min
-
Bend radius 180*
t
-
Bend radius 90*
t
2,5
Brinell Hardness
HBS
94
Thickness interval
Min
1.5
Max
3
Tensile strength (Rm) MPa
Min
310
Max
-
Proof stress (Rp0,2)
MPa
260
Elongation A50mm
% min
7
Elongation
% min
-
Bend radius 180*
t
-
Bend radius 90*
t
3,5
Brinell Hardness
HBS
94
Thickness interval
Min
3
Max
6
Tensile strength (Rm) MPa
Min
310
Max
-
Proof stress (Rp0,2)
MPa
260
Elongation A50mm
% min
10
Elongation
% min
-
Bend radius 180*
t
-
Bend radius 90*
t
4,5
Brinell Hardness
HBS
94
Thickness interval
Min
6
Max
12.5
Tensile strength (Rm) MPa
Min
300
Max
-
Proof stress (Rp0,2)
MPa
255
Elongation A50mm
% min
9
Elongation
% min
-
Bend radius 180*
t
-
Bend radius 90*
t
6
Brinell Hardness
HBS
91
Thickness interval
Min
12.5
Max
60
Tensile strength (Rm) MPa
Min
295
Max
-
Proof stress (Rp0,2)
MPa
240
Elongation A50mm
% min
-
Elongation
% min
8
Bend radius 180*
t
-
Bend radius 90*
t
-
Brinell Hardness
HBS
89
Thickness interval
Min
60
Max
100
Tensile strength (Rm) MPa
Min
295
Max
-
Proof stress (Rp0,2)
MPa
240
Elongation A50mm
% min
-
Elongation
% min
7
Bend radius 180*
t
-
Bend radius 90*
t
-
Brinell Hardness
HBS
89
Thickness interval
Min
100
Max
150
Tensile strength (Rm) MPa
Min
275
Max
-
Proof stress (Rp0,2)
MPa
240
Elongation A50mm
% min
-
Elongation
% min
6
Bend radius 180*
t
-
Bend radius 90*
t
-
Brinell Hardness
HBS
84
Thickness interval
Min
150
Max
175
Tensile strength (Rm) MPa
Min
275
Max
-
Proof stress (Rp0,2)
MPa
230
Elongation A50mm
% min
-
Elongation
% min
4
Bend radius 180*
t
-
Bend radius 90*
t
-
Brinell Hardness
HBS
83
Thickness interval
Min
175
Max
350
Tensile strength (Rm) MPa
Min
260
Max
-
Proof stress (Rp0,2)
MPa
220
Elongation A50mm
% min
-
Elongation
% min
2
Bend radius 180*
t
-
Bend radius 90*
t
-
Brinell Hardness
HBS
-