EN AW-7075

Plate length

1020 x 2020 mm

Thickness

100.0 mm

Temper

T6

We stock a wide range of plates. They are in many different alloys; however, the most common are 5754, 5083 and 6082. Do you request other thickness or alloy types than the once introduced - you are welcome to contact us.  


  • Plate length: 1020 x 2020 mm
  • Thickness: 100.0 mm
  • Temper: T6
  • Weldability: Medium
  • Corrosion: Low
  • Cut/drilling: High
  • Surface: Low
On request

EN AW-7075

Is a short-chipped alloy with a very high strength. The alloy has a low corrosion resistance and a low welding- and anodizing level.


We are not liable for items out of stock. The specified weight is theoretical. Please contact us if you have any further enquiries.

Alloy - Alloys

Si
Min
-
Max
0.4
Fe
Min
-
Max
0.5
Cu
Min
1.2
Max
2
Mn
Min
-
Max
0.3
Mg
Min
2.1
Max
2.9
Cr
Min
0.18
Max
0.28
Zn
Min
5.1
Max
6.1
Ti
Min
-
Max
0.2
Others
Min
0.15
Max
-

Alloy - Aluminium Properties

Alloy
EN AW-7075
Temper
O
Thermal conductivity
W/m*K
175
Coefficient of thermal expansion
µm/(m*K)
23,5
Annealing
Min
-
Annealing
Max
-
Melting point
Min
475
Max
635
Melting point
Max
635
Elastic modulus
KN/mm2
72
Electrical conductivity
%IACS
45,5
Alloy
EN AW-7075
Temper
T6
Thermal conductivity
W/m*K
134
Coefficient of thermal expansion
µm/(m*K)
23,5
Annealing
Min
-
Annealing
Max
-
Melting point
Min
475
Max
635
Melting point
Max
635
Elastic modulus
KN/mm2
72
Electrical conductivity
%IACS
33
Alloy
EN AW-7075
Temper
T7
Thermal conductivity
W/m*K
155
Coefficient of thermal expansion
µm/(m*K)
23,5
Annealing
Min
-
Annealing
Max
-
Melting point
Min
475
Max
635
Melting point
Max
635
Elastic modulus
KN/mm2
72
Electrical conductivity
%IACS
39,5

Alloy - Mechanical Properties (EN 485-2:2008)

Thickness interval
Min
0.4
Max
0.8
Tensile strength (Rm) MPa
Min
525
Max
-
Proof stress (Rp0,2)
MPa
460
Elongation A50mm
% min
6
Elongation
% min
-
Bend radius 180*
t
-
Bend radius 90*
t
4,5
Brinell Hardness
HBS
157
Thickness interval
Min
0.8
Max
1.5
Tensile strength (Rm) MPa
Min
540
Max
-
Proof stress (Rp0,2)
MPa
460
Elongation A50mm
% min
6
Elongation
% min
-
Bend radius 180*
t
-
Bend radius 90*
t
5,5
Brinell Hardness
HBS
160
Thickness interval
Min
1.5
Max
3
Tensile strength (Rm) MPa
Min
540
Max
-
Proof stress (Rp0,2)
MPa
470
Elongation A50mm
% min
7
Elongation
% min
-
Bend radius 180*
t
-
Bend radius 90*
t
6,5
Brinell Hardness
HBS
161
Thickness interval
Min
3
Max
6
Tensile strength (Rm) MPa
Min
545
Max
-
Proof stress (Rp0,2)
MPa
475
Elongation A50mm
% min
8
Elongation
% min
-
Bend radius 180*
t
-
Bend radius 90*
t
8
Brinell Hardness
HBS
163
Thickness interval
Min
6
Max
12.5
Tensile strength (Rm) MPa
Min
540
Max
-
Proof stress (Rp0,2)
MPa
460
Elongation A50mm
% min
8
Elongation
% min
-
Bend radius 180*
t
-
Bend radius 90*
t
12
Brinell Hardness
HBS
160
Thickness interval
Min
12.5
Max
25
Tensile strength (Rm) MPa
Min
540
Max
-
Proof stress (Rp0,2)
MPa
470
Elongation A50mm
% min
-
Elongation
% min
6
Bend radius 180*
t
-
Bend radius 90*
t
-
Brinell Hardness
HBS
161
Thickness interval
Min
25
Max
50
Tensile strength (Rm) MPa
Min
530
Max
-
Proof stress (Rp0,2)
MPa
460
Elongation A50mm
% min
-
Elongation
% min
5
Bend radius 180*
t
-
Bend radius 90*
t
-
Brinell Hardness
HBS
158
Thickness interval
Min
50
Max
60
Tensile strength (Rm) MPa
Min
525
Max
-
Proof stress (Rp0,2)
MPa
440
Elongation A50mm
% min
-
Elongation
% min
4
Bend radius 180*
t
-
Bend radius 90*
t
-
Brinell Hardness
HBS
155
Thickness interval
Min
60
Max
80
Tensile strength (Rm) MPa
Min
495
Max
-
Proof stress (Rp0,2)
MPa
420
Elongation A50mm
% min
-
Elongation
% min
4
Bend radius 180*
t
-
Bend radius 90*
t
-
Brinell Hardness
HBS
147
Thickness interval
Min
80
Max
90
Tensile strength (Rm) MPa
Min
490
Max
-
Proof stress (Rp0,2)
MPa
390
Elongation A50mm
% min
-
Elongation
% min
4
Bend radius 180*
t
-
Bend radius 90*
t
-
Brinell Hardness
HBS
144
Thickness interval
Min
90
Max
100
Tensile strength (Rm) MPa
Min
460
Max
-
Proof stress (Rp0,2)
MPa
360
Elongation A50mm
% min
-
Elongation
% min
3
Bend radius 180*
t
-
Bend radius 90*
t
-
Brinell Hardness
HBS
135
Thickness interval
Min
100
Max
120
Tensile strength (Rm) MPa
Min
410
Max
-
Proof stress (Rp0,2)
MPa
300
Elongation A50mm
% min
-
Elongation
% min
2
Bend radius 180*
t
-
Bend radius 90*
t
-
Brinell Hardness
HBS
119
Thickness interval
Min
120
Max
150
Tensile strength (Rm) MPa
Min
360
Max
-
Proof stress (Rp0,2)
MPa
260
Elongation A50mm
% min
-
Elongation
% min
2
Bend radius 180*
t
-
Bend radius 90*
t
-
Brinell Hardness
HBS
104
Thickness interval
Min
150
Max
200
Tensile strength (Rm) MPa
Min
360
Max
-
Proof stress (Rp0,2)
MPa
240
Elongation A50mm
% min
-
Elongation
% min
2
Bend radius 180*
t
-
Bend radius 90*
t
-
Brinell Hardness
HBS
-
Thickness interval
Min
200
Max
300
Tensile strength (Rm) MPa
Min
360
Max
-
Proof stress (Rp0,2)
MPa
220
Elongation A50mm
% min
-
Elongation
% min
1
Bend radius 180*
t
-
Bend radius 90*
t
-
Brinell Hardness
HBS
-