EN AW-5005

Material id: 1101208

Nature Anodized 15 µ

Plate length

1250 x 2500 mm

Thickness

1.5 mm

Temper

H14

We stock a wide range of anodised plates in standard thickness between 1 mm and 3 mm. Our standard range features the most popular μ- thickness without colour, but do you request colouring or another thickness - you are welcome to contact us.


  • Plate length: 1250 x 2500 mm
  • Thickness: 1.5 mm
  • Temper: H14
  • Weldability: High
  • Corrosion: High
  • Cut/drilling: Medium
  • Surface: High

EN AW-5005

It is good for machining and bending and has a high corrosion resistance and good for welding. The alloy is very suitable for decorative anodizing.


We are not liable for items out of stock. The specified weight is theoretical. Please contact us if you have any further enquiries.

Alloy - Alloys

Si
Min
-
Max
0.3
Fe
Min
-
Max
0.7
Cu
Min
-
Max
0.2
Mn
Min
-
Max
0.2
Mg
Min
0.5
Max
1.1
Cr
Min
-
Max
0.1
Zn
Min
-
Max
0.25
Others
Min
0.15
Max
-

Alloy - Aluminium Properties

Alloy
EN AW-5005
Temper
Hx2
Thermal conductivity
W/m*K
201
Coefficient of thermal expansion
µm/(m*K)
23,5
Annealing
Min
-
Annealing
Max
-
Melting point
Min
630
Max
655
Melting point
Max
655
Elastic modulus
KN/mm2
70
Electrical conductivity
%IACS
52
Alloy
EN AW-5005
Temper
Hx4
Thermal conductivity
W/m*K
201
Coefficient of thermal expansion
µm/(m*K)
23,5
Annealing
Min
-
Annealing
Max
-
Melting point
Min
630
Max
655
Melting point
Max
655
Elastic modulus
KN/mm2
70
Electrical conductivity
%IACS
52
Alloy
EN AW-5005
Temper
Hx6
Thermal conductivity
W/m*K
201
Coefficient of thermal expansion
µm/(m*K)
23,5
Annealing
Min
-
Annealing
Max
-
Melting point
Min
630
Max
655
Melting point
Max
655
Elastic modulus
KN/mm2
70
Electrical conductivity
%IACS
52
Alloy
EN AW-5005
Temper
Hx8
Thermal conductivity
W/m*K
201
Coefficient of thermal expansion
µm/(m*K)
23,5
Annealing
Min
-
Annealing
Max
-
Melting point
Min
630
Max
655
Melting point
Max
655
Elastic modulus
KN/mm2
70
Electrical conductivity
%IACS
52
Alloy
EN AW-5005
Temper
Hx9
Thermal conductivity
W/m*K
201
Coefficient of thermal expansion
µm/(m*K)
23,5
Annealing
Min
-
Annealing
Max
-
Melting point
Min
630
Max
655
Melting point
Max
655
Elastic modulus
KN/mm2
70
Electrical conductivity
%IACS
52
Alloy
EN AW-5005
Temper
O
Thermal conductivity
W/m*K
201
Coefficient of thermal expansion
µm/(m*K)
23,5
Annealing
Min
-
Annealing
Max
-
Melting point
Min
630
Max
655
Melting point
Max
655
Elastic modulus
KN/mm2
70
Electrical conductivity
%IACS
52

Alloy - Mechanical Properties (EN 485-2:2008)

Thickness interval
Min
0.2
Max
0.5
Tensile strength (Rm) MPa
Min
145
Max
185
Proof stress (Rp0,2)
MPa
120
Elongation A50mm
% min
2
Elongation
% min
-
Bend radius 180*
t
2
Bend radius 90*
t
0,5
Brinell Hardness
HBS
48
Thickness interval
Min
0.5
Max
1.5
Tensile strength (Rm) MPa
Min
145
Max
185
Proof stress (Rp0,2)
MPa
120
Elongation A50mm
% min
2
Elongation
% min
-
Bend radius 180*
t
2
Bend radius 90*
t
1
Brinell Hardness
HBS
48
Thickness interval
Min
1.5
Max
3
Tensile strength (Rm) MPa
Min
145
Max
185
Proof stress (Rp0,2)
MPa
120
Elongation A50mm
% min
3
Elongation
% min
-
Bend radius 180*
t
2,5
Bend radius 90*
t
1
Brinell Hardness
HBS
48
Thickness interval
Min
3
Max
6
Tensile strength (Rm) MPa
Min
145
Max
185
Proof stress (Rp0,2)
MPa
120
Elongation A50mm
% min
4
Elongation
% min
-
Bend radius 180*
t
-
Bend radius 90*
t
2
Brinell Hardness
HBS
48
Thickness interval
Min
6
Max
12.5
Tensile strength (Rm) MPa
Min
145
Max
185
Proof stress (Rp0,2)
MPa
120
Elongation A50mm
% min
5
Elongation
% min
-
Bend radius 180*
t
-
Bend radius 90*
t
2,5
Brinell Hardness
HBS
48