EN AW-3103

Varenummer: 1000116

Width

1000.0 mm

Thickness

0.63 mm

Weight

250.0 mm

We offer coils in the standard thickness from 0.63 mm to 1 mm. We deliver all our coils in the standard width of 1000 mm and basic, we can deliver in three standard sizes: 250 kg, 500 kg and 1000 kg. If you request further information or other dimensions - you are welcome to contact us.


  • Width: 1000.0 mm
  • Thickness: 0.63 mm
  • Weight: 250.0 mm
  • Weldability: High
  • Corrosion: High
  • Cut/drilling: Low
  • Surface: Medium

EN AW-3103

A manganese alloy with a high corrosion resistance. The alloy has an average strength and is suitable for welding and bending.


We are not liable for items out of stock. The specified weight is theoretical. Please contact us if you have any further enquiries.

Alloy - Alloys

Si
Min
-
Max
0.5
Fe
Min
-
Max
0.7
Cu
Min
-
Max
0.1
Mn
Min
0.9
Max
1.5
Mg
Min
-
Max
0.3
Cr
Min
-
Max
0.1
Zn
Min
-
Max
0.2
Al
Min
0.15
Max
-

Alloy - Aluminium Properties

Alloy
EN AW-3103
Temper
Hx2
Thermal conductivity
W/m*K
160
Coefficient of thermal expansion
µm/(m*K)
23,1
Annealing
Min
-
Annealing
Max
-
Melting point
Min
640
Max
655
Melting point
Max
655
Elastic modulus
KN/mm2
70
Electrical conductivity
%IACS
42
Alloy
EN AW-3103
Temper
Hx4
Thermal conductivity
W/m*K
160
Coefficient of thermal expansion
µm/(m*K)
23,1
Annealing
Min
-
Annealing
Max
-
Melting point
Min
640
Max
655
Melting point
Max
655
Elastic modulus
KN/mm2
70
Electrical conductivity
%IACS
42
Alloy
EN AW-3103
Temper
Hx6
Thermal conductivity
W/m*K
160
Coefficient of thermal expansion
µm/(m*K)
23,1
Annealing
Min
-
Annealing
Max
-
Melting point
Min
640
Max
655
Melting point
Max
655
Elastic modulus
KN/mm2
70
Electrical conductivity
%IACS
42
Alloy
EN AW-3103
Temper
Hx8
Thermal conductivity
W/m*K
160
Coefficient of thermal expansion
µm/(m*K)
23,1
Annealing
Min
-
Annealing
Max
-
Melting point
Min
640
Max
655
Melting point
Max
655
Elastic modulus
KN/mm2
70
Electrical conductivity
%IACS
42
Alloy
EN AW-3103
Temper
Hx9
Thermal conductivity
W/m*K
160
Coefficient of thermal expansion
µm/(m*K)
23,1
Annealing
Min
-
Annealing
Max
-
Melting point
Min
640
Max
655
Melting point
Max
655
Elastic modulus
KN/mm2
70
Electrical conductivity
%IACS
42
Alloy
EN AW-3103
Temper
O
Thermal conductivity
W/m*K
190
Coefficient of thermal expansion
µm/(m*K)
23,1
Annealing
Min
-
Annealing
Max
-
Melting point
Min
640
Max
655
Melting point
Max
655
Elastic modulus
KN/mm2
70
Electrical conductivity
%IACS
50,5