EN AW-2007

Diameter

25 mm

Length

3000.0 mm

Process

Extruded

We stock a wide range of round bars in 2000 og 6000 alloys Essentially, they exist in all sizes from 5 mm and up to 500 mm in diameter, and often in lengths of 3000 mm and 6000 mm and in three different qualities: pressed, drawn and moulded. If you request other dimensions than the once introduced - you are welcome to contact us


  • Diameter: 25 mm
  • Length: 3000.0 mm
  • Process:
  • Weight: 1.40 kg/m
  • Weldability: Low
  • Corrosion: Low
  • Cut/drilling: High
  • Surface: Low
In stock

EN AW-2007

A copper alloy that typically contains between 4.0 and 5.0 % copper, and it is suitable for producing machine parts, bolts and rivets. It looks very much like EN AW-2011, but it is yet a bit harder. It is a short-chipped alloy, which is suitable for treatment, threads and high machining speeds. The alloy has a low corrosion resistance and is not suitable for welding because of the high content of copper. It is not approved by the ROHS.


We are not liable for items out of stock. The specified weight is theoretical. Please contact us if you have any further enquiries.

Alloy - Alloys

Si
Min
0.4
Max
0.8
Fe
Min
-
Max
0.8
Cu
Min
3.3
Max
4.6
Mn
Min
0.5
Max
1
Mg
Min
0.4
Max
1.8
Cr
Min
-
Max
0.1
Zn
Min
-
Max
0.2
Ni
Min
-
Max
0.2
Bi
Min
-
Max
0.2
Pb
Min
0.8
Max
1.5
Sn
Min
0.2
Max
-
Others
Min
0.3
Max
-

Alloy - Aluminium Properties

Alloy
EN AW-2007
Temper
T3
Thermal conductivity
W/cm*K
130,0
Coefficient of thermal expansion
µm/(m*K)
23,0
Annealing
Min
-
Annealing
Max
-
Melting point
Min
510
Max
640
Melting point
Max
640
Elastic modulus
KN/mm2
72500
Electrical conductivity
%IACS
34,0
Alloy
EN AW-2007
Temper
T4
Thermal conductivity
W/cm*K
130,0
Coefficient of thermal expansion
µm/(m*K)
23,0
Annealing
Min
-
Annealing
Max
-
Melting point
Min
510
Max
640
Melting point
Max
640
Elastic modulus
KN/mm2
72500
Electrical conductivity
%IACS
34,0

Alloy - Mechanical Properties (EN 755-2:2013)

Dimension
Min
-
Max
80
Tensile strength (Rm) MPa
Min
370
Max
-
Proof stress (Rp0,2)
MPa
250
Elongation A50
% min
6
Elongation A
% min
8
Brinell hardness
HBS
95
Dimension
Min
80
Max
200
Tensile strength (Rm) MPa
Min
340
Max
-
Proof stress (Rp0,2)
MPa
220
Elongation A50
% min
-
Elongation A
% min
8
Brinell hardness
HBS
95
Dimension
Min
200
Max
250
Tensile strength (Rm) MPa
Min
330
Max
-
Proof stress (Rp0,2)
MPa
210
Elongation A50
% min
-
Elongation A
% min
7
Brinell hardness
HBS
95