Roller Tubes |
|
|
| |
|
High quality – Efficient production
High quality roller tubes have great importance for our customers as these tubes help to optimise the production process. This tube is in fact characterised by its fine tolerances on outside and inside diameters, uniform thickness and concentric running accuracy. The material consumption is reduced and an economical production is achieved.
Roller tubes are supplied in alloy EN AW-6060, and in 3 different qualities:
- T.O.P.-quality
- H.T.- quality
- I.S.Q.- quality
Delivery time about 1 week. |
|
|
| |
|
Roller Tubes - EN AW-6060 T6
Manufacturing length 6010 mm
EN 755-1, 755-2 |
 | |
| |
|
|
|
 |
Can also be supplied cut to length.
All stated weights are theoretical weights, which may vary. |
|
| |
|
Please allow approx. 1-2 weeks´delivery time for dimensions no in stock. |
|
|
| | | |
|
Roller Tubes
T.O.P. – quality:
Material 6060
|
|
|
Roller Tubes
H.T. – quality:
Material 6060
|
|
|
Roller Tubes
I.S.Q. – quality:
Material 6060
|
| |
|
|
|
|
|
|
|
Temper-hardened
Strength T6 |
|
|
Temper-hardened
Strength T6 |
|
|
Temper-hardened
Strength T6 |
|
| |
|
|
|
|
|
|
|
Type:
Hot-extruded via chamber mould and drawn |
|
|
Type:
Hot-extruded via chamber mould and drawn |
|
|
Type:
Hot-extruded via chamber mould and drawn |
|
| |
|
|
|
|
|
|
|
| Tolerances: |
|
|
Tolerances: |
|
|
Tolerances: |
|
| Outside diameter |
ISO k 13 |
|
Outside diameter |
ISO k 15 |
|
Outside diameter |
ISO k 14 |
| Inside diameter |
ISO H 11 |
|
Inside diameter |
ISO M 15 |
|
Inside diameter |
ISO H 14 |
| Inequality of wall in % of the nominal wall thickness |
|
|
Inequality of wall in % of the nominal wall thickness |
|
|
Inequality of wall in % of the nominal wall thickness |
|
| S < 7 mm |
6% |
|
S > 10 mm |
5% |
|
S < 10 mm |
5% |
| S > 7 mm |
5% |
|
|
|
|
|
|
| |
|
|
|
|
|
|
|
| Straightness: |
0,2 mm/m |
|
Straightness: |
0,5 mm/m |
|
Straightness: |
|
| |
|
|
|
|
|
D < 250 mm |
0,6 mm |
| |
|
|
|
|
|
D > 250 mm |
0,8 mm/m |
| |
|
|
|
|
|
|
| | | | |